Question. Is there software that can convert selected electron diffraction patterns into Euler angles ?

13 September 2021 1 7K Report

I want to caculate the misoriention between two adjacent grains. Now, i have obtained the SADP of two grains.

There is an EBSD-like system for TEM, that builds orientation maps from the SAED patterns data. Check Astar at www.nanomegas.com

Badges
Science topic

More Zhifu Yao's questions See All

Why the fatigue life at high temperature could be higher than that at room temperature?

I carried out low-cycle fatigue tests on a secondary-hardenning ultra-high-strength steel with test condition εmax = 0.9%. It was found that the fatigue life at high temperature was much higher...

29 May 2024 3,176 1 View

How do researchers avoid over-amplification of eukaryotic chloroplast 16S rDNA?

How do researchers avoid over-amplification of eukaryotic chloroplast 16S rDNA when classifying prokaryotic microbial communities in algal bloom experiments? For example, if I need to amplify...

07 April 2024 3,064 0 View

What are the perceptions of TVET graduates regarding the integration and utilization of technology in their educational curriculum?

TVET graduates perceive the incorporation of technology into their educational programs. It delves into their attitudes towards technology and its role in their vocational training.

06 March 2024 5,116 1 View

Input resistance changes in whole-cell current clamp mode?

Dear community: I would like to seek opinions from you on current-clamp mode in electrophysiology. I am trying to record voltage response from neurons, so I first do whole-cell recordings on...

24 January 2024 9,549 4 View

How much antibody do I need for large volume sample in FACS?

Hi, I'd like to stain 10M cells with CD3 for cell sorting. The datasheet says 5ul/test, and typically use 1 × 10^6 cells in a 100-µl experimental sample (a test). So does it mean I need a 50ul...

26 October 2023 5,300 2 View

How to set damage value threshold in the MAT_RHT?

topic: the concrete material model RHT in LS-DYNA I see some scholars mentioned the damage value threshold Dcr, but I don not know where to set it, and find no relative paramaters in 072MAT_RHT....

06 August 2023 1,660 1 View

When I use Nvidia Quantum Espresso SIF image, it can not find ph.x. What should I do?

As below: INFO: Using cached SIF image INFO: MPS server daemon started INFO: Running QE with: 2 GPUs 4 MPI processes total 2 MPI processes per GPU 2 Pools 2 KPoints + mpirun -n 4 ph.x...

20 June 2023 187 0 View

Could anyone provide some practical LS-DYNA models for learning?

09 June 2023 6,846 1 View

Can you help me find a FORTRAN code that simulates a PV module with fins or PVT sensor with fins?

Hello Researchers I would like to perform the 2D simulation of a PVT system with fins using FORTRAN. I therefore ask for help for anyone who has it or who knows a website where I can find it. The...

30 April 2023 357 2 View

The content of dry weight of microalgae under mixtrophic or heterotrophic, which one is higher?

i found the content of dry weight of euglena gracilis under mixtrophic is much higher than than under heterotrophic. almost 2-fold. is that right?or something wrong happened?

23 April 2023 1,902 1 View

How can I prepare virus for a TEM or SEM imaging?

I have virus (viral hemorrhagic septicemia virus) in suspension and the experiment will not involve cells. What level of TCID50 is preferred?

11 August 2024 3,115 1 View

I need JCPDS file of LSFCO nanomaterial. Can anyone provide me?

Require for Rietveld refinement in XRD.

08 August 2024 3,081 2 View

1. If I can quantize the atom using this hyperbolic spiral and classical physics, could nature do the same?

If we map as a continuous motion an ionising electron (beginning its journey at n=1) in an H atom, a specific hyperbolic spiral appears (see animation). When we solve this spiral formula, we find...

07 August 2024 5,343 2 View

Is there anyone with experience in TEM analysis who can assist with a manuscript for an upcoming journal?

Hello dear colleagues, We have prepared a manuscript on NiTi-based alloys and are seeking a second opinion on our current TEM results. If you are a Ph.D. holder with experience in TEM and have...

07 August 2024 9,563 0 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

How to fix background error in rietveld refinement of one XRD peak using GSAS-II?

I want to refine one XRD peak of my in-situ xrd but the background is never working good which ultimately fails the refinement. How to refine and adjust the background using GSAS-II

05 August 2024 5,291 2 View

Which distribution type should I use when calculating the average particle size from TEM image? and how to calculate the error ?

average particle size calculation from TEM

04 August 2024 2,921 1 View

Why reactivity isn't increased with more empty spots in valence shell?

If from a geometric perspective the non-halogens, non-noble gases have more empty spots in their valence shell, and the filling/exiting of any of the empty spots in the shell constitutes a...

03 August 2024 4,787 2 View

Why is the molecule's orientation with an electric field affect polarizability?

Why is the molecule's orientation with an electric field affect polarizability? Electrons are diffuse enough to be independent with respect to orientation and effect of electric field on...

03 August 2024 7,843 1 View

Why doesn't chromium 2+ ion use all its d-orbitals to receive lone pairs from six waters in [Cr(H20)6)]3+?

I'm guessing it's because the ligand experiences too much electron repulsion or proton repulsion from the chromium to insert them close to the 3d-orbitals which are close to the metal nucleus. Is...

03 August 2024 1,370 1 View