When the gold ions are getting reduced to AuNPs, Is it possible that the (111) diffraction plane doesn't develop and other reflection planes like (200), (220), and (311) get constructed? Is it possible? If so how? Does it depend on the stabilizing agent and other synthesis factors?
Sai Prasad Nayak
Thanks for the reply. The XRD was carried out from 2theta of 10-80 deg with a step size of 0.001. The XRD scan was done on 3 samples attached below. Where I see only sample-C with appropriate FCC peaks whereas for sample A/B, there was no sign of (111) peak, and other peaks were shifted. I think there was no proper development of the diffraction planes in A/B. What's your view on this?