I need perfect cleanliness for further processes but I am not sure which cleaning method would be sufficient yet letting the layers intact.
you could clean the wafer by using BOE or diluted HCl
but BoE use should be careful because of Ti etch
Less aggressive cleaning can be done using aceton and IPA solvents.
I am trying to quantify Parylene C's hermetic encapsulation quality using EIS with a 2 electrode configuration (WE/WS and RE/CE). I am simply using two patterned gold layers on glass as my...
12 January 2021 7,399 14 View
A simple definition might help to understand the diffraction pattern in an aperiodic nano-micro structured surface.
19 July 2018 3,865 6 View
01 June 2016 5,159 3 View
24 December 2015 6,303 4 View
24 November 2015 8,669 6 View
24 November 2015 8,487 5 View
Can tuning roughness leads to different stiffness of a material?
18 October 2015 3,286 8 View
As trypan blue fails to calculate the accurate viability rate of my [cell+alginate 1.2%] suspension, I was thinking about using dual florescent dye (PI & AO). However, I am concerned about whether...
22 February 2013 5,130 2 View
While encapsulating ADMSCs in sodium alginate, providing a 3D environment for the cells, I come across different viability rates. Trypan blue shows a lower viability rate, as low as 50%. On the...
19 February 2013 6,200 5 View
I am using a Sutter electrode holder for my patch clamp experiments, but I'm having trouble keeping positive pressure inside my electrode due to a leak out of the back of the holder. I have added...
02 March 2021 5,829 1 View
I want to do RF sputtering of ITO on glass substrate using magnetron sputtering. what thickness do i need to make it good conductive layer to use it for PSC. Moreover, whats about thickness of...
01 March 2021 395 3 View
I am conducting anodic electrodeposition of MnO2 onto a stainless steel substrate, using a platinum strip as a counter electrode. This is done galvanostatically, with the current held between 5...
27 February 2021 1,829 3 View
Good day to all, I have no experience with light emitting diodes. I am building a glass mini flume to demonstrate the photo degradation of Methylene Blue in water running over self cleaning...
26 February 2021 4,026 5 View
During performing CV of a GCE or modified GCE, we rise the potential in the first half of the cycle and reduce it in reverse half. During the first half, what is the nature of charge on GCE or...
25 February 2021 7,994 3 View
I am trying to characterize an electrochromic system. The system uses ITO electrodes on glass, WO3 as the electrochromic film, and NiO as the ion storage layer. When I deposit NiO and WO3 and...
23 February 2021 9,592 2 View
I need to clean the hydrocarbon contamination on the carbon substrate of TEM grid. However, I heard that substrate could be broken by the powerful plasma. My substrate is pure carbon, with ~3nm,...
23 February 2021 3,262 5 View
What are the testing rate for electrodes recommended by ASTM for cochlear implants. I am currently doing the 15mm/min elongatio testing.
22 February 2021 1,515 1 View
One of my colleagues said, "the impedance you can measure with the three electrodes and with the specific sequence varying the frequency" Is it possible to configure the potenciostat without the...
21 February 2021 418 2 View
Hello everyone Do you have any information about this error 'The experiment was stopped by a potential overload on Vs (auxiliary electrode)' in Origamaster software? I tried everything possible,...
19 February 2021 3,152 7 View