Hello Sarah,

first of all what magnification would you like to get? Do you want to see nanoparticles? 

Some problems you can get with TiO2 is the rather poor conductivity, so a low current would give better results. If the magnification it very high it is also good to cool the sample with liquid nitrogen, if the microscope allows it.

I hope I could help you