Due to large deformation of rubber like material there is significant difference in stress-strain curve obtained theoretically and experimentally. It is difficult to predict which, hyperelastic material model is accurate for the particular rubber like material. However based on literature available;

Based on experimental results i.e. Uni-axial test results are in good agreement with the strain responses predicted by different models like Mooney-Rivlin model, and Yeoh model at specific strain rate. Neo-Hookean model is not so suitable for uni-axial tensile test of elastomeric material as compare to other models. Neo-Hookean Model is accurate only for small strain.

Neo- Hookean: this method can be used if the data is insufficient. like if we do not have C01. useful if we have small stain data

Ogden: Can be used by stiffness of strain-stress curve for large deformation maerial

Mooney- Rivlin Model : is more useful by using hear behavior and uniaxial strain of the material

файл subtopics.txt - 20 topics from scientific articles on model hyperelastic material

Here are 20 topics from the articles which contain words ” model hyperelastic material " in their titles. Each topic is presented with 20 words and 20 phrases as it is done in these articles.

As from previous experience not more then 30% of these topics will be useful for you.

Reading these topics will require efforts from you, since this is not a coherent presentation, and each topic is a list of substances, methods, theories, cases, etc. associated with this topic. Try to be patient, in the hope that new hypotheses and thoughts will appear.

Feel free to make Feedback