The name says it: SAED - selected area electron diffraction ... correlate your diffraction pattern with the selected area of the image! I do not know what you're interested and why you have trouble to do this pattern: Impuritiy phases, orientation relation, grain boundaries, interlayers, particle size .... You can use this pattern to switch to dark field imaging .... Best you collect some ideas with help of the Williams: