If structure like Titania having crystalline core and disordered layer or amorphous with specific surface area get decrease from 50 m2/g to 30 m2/g. definetly its particle size will increase but due to disorderness at the surface intensity of XRD will decrease and FWHM will increased so Crystallite size may be decreased. If any article anyone suggest Please give suggestion.