Dear researchers, i hope you all are doing well. Currently i am working on Cu and Ni foam based electrode for MXenes based supercapacitors and my material is in powder form. But i have no idea to make working electrode for supercapacitors from them. Is there any friend who worked on Cu or Ni foam before or still working. Can you guide me the whole procedure ?
your quick and positive response will be highly appreciated. Thanks
Hi Ubaid Khan,
Generally MXene material don't need a binder material if you synthesis using Li + HCl (clay will form) from MAX phase. If you have directly power form of MXene then add PVDF binder and make a slurry and then use drop-casting method to coat electrode material on Cu or Ni form.
Dear Ubaid,
your question is specific. However, try these articles; I hope you will find some useful ideas: