On the work with the growth technique of Chemical Bath Deposition:
Has someone studied or identified the problem encountered when we place a (supposed stable) thin film of a semiconductor poly-crystalline material inside of the solution which the Chemica Bath will be performed, when we want to grow a second material above a previous one ?
e.i. to grow PbS on a CdS thin films (also previously growth by CBD), we immerse the CdS thin film on the solution, and the surface material of the first film gets unstable, and disolves and diffuses on the chemical solution of PbS.
Has someone studied/identified this studying the electrical performance (or other kind) of a diode device like a solar cell or diode of other kind?
Thanks C. Das for your comments, I will work on it and see in what way I can vary these parameters in my Bath.
It was interesting you used the words "electrolite" and "potential" ... I have' nt seen before the Chem. Bath as the electrolyte ... Would you say, there is an important Electrochemical Potential on my Bath ? Do you think to try to measure this potential could be helpful ?
I also looked for the Pourbaix diagrams, Do you know them sir?
If there is an considerable electrochemical potential on my soution , maybe the Pourbaix diagram (elec.potential vs. pH) could be helpful .
Thank you for your comments :)
Regards !