Dear Colleagues,
I humbly request for an urgent support.
I have many ZTA compositions added with different oxides. However, when I insert them into Highscore X'Pert software, it is obvious that there many shifting of (2 Theta) angles for many of XRD pattern. To make a correct comparison between them, I need to displace these XRD patterns belong to the shifted 2 theta angles to their correct locations.
I will be grateful to let me know how to perform this task in Highscore X'Pert? what tab, function or steps I should use to start the correction?
Thank you in advance.
Zhwan
Hey there,
you need to go to Treatment - Adjust to anchor. The anchor scan is the one highlighted in red in the Scan list. You modify the other scans to fit the anchor scan. Sometimes, it works better to use the Manual setting and to input the off-set value yourself.
Good luck
Eliska
Thank you dear Eliška Skořepová I have found the solution for that case . It can be adjusted from scan list.
Thank you for explanation. Kindly, look at the attached file