You may try adding a modifier element to the melt, such as Mg or Ca, to lower the surface tension of the Al-rich melt, to facilitate the dispersion of the intermetallic particles in your final product. Below, a paper shows this effect on SiC particles.

http://dergipark.gov.tr/download/article-file/126706