I want to make thermal reduced graphene oxide RGO from graphite oxide prepared by modifies Hummer's method. How can do the exfoliation and what is the procedure to perform the thermal reduction under argon atmosphere.
A graphene oxide was placed into a quartz furnace crucible at different temperatures 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
A graphene oxide was placed into a quartz furnace crucible at different temperatures 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
A graphene oxide was placed into a quartz furnace crucible at different temperatures 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
A graphene oxide was placed into a quartz furnace crucible at different temperatures 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
A graphene oxide was placed into a quartz furnace crucible at different temperatures about 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
A graphene oxide was placed into a quartz furnace crucible at different temperatures about 900 - 1100°C for 30 minunes under a flow of laminar H2 gas(99.999%).to prepare thermal reduced graphene oxide.
Dr. shen Ming
first if you have an image of the quartz furnace crucible, it will be better because I did not know how it look like.
Second, What about exfoliation of the Graphite oxide. Does I put the graphite oxide directly without exfoliation.