Hello everyone, I want to grow thin film on FTO using hydrothermal but the medium is highly basic so FTO looses even its own stability and tore down into small pieces. Now my question ' is there any most stable substrate that could even stable in highly basic conditions? because my sample with specific morphology could be obtained hydrothermally in highly basic medium like 16M KOH solution. If anyone could give some suggestions will be highly appreciated. Thank you