Cut PDMS sheet with Graphtec cutter plotter CE6000-40?

26 June 2024 1 8K Report

Dear All,

I want to cut PDMS sheet with thickness of 0.8 mm to rectangular shape with Graphtec cutter plotter CE6000-40. What condition do you offer? Do you offer any kind of special speed or force?

Maryam Ansari

Thank you so much for your help.

Badges
Science topic

Similar topics
Econ
Manufacturing
Industry

More Maryam Ansari's questions See All

Leaf area of tomato ?

Hi How can this equation Ln(LA) = 1.038 + 0.89 ln(X) be applied to calculate the leaf area of a tomato? Can you explain with an example and what is the substitution of Ln and ln?

06 August 2024 2,508 2 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

If we are using snowball sampling technique, how do we justify the true representativeness of the sample statistically? is there any statistical test?

Are there any statistical methods to justify your sampling technique using SPSS or AMOS?

05 August 2024 9,153 4 View

How to retain amplicon yield after Ampure bead cleanup, following a 2-stage PCR protocol?

Hello all, I have been trying to follow a 2-stage PCR protocol used to amplify barcodes of a large yeast library, as per Nyugen et al. (2022) -...

30 July 2024 841 2 View

How to add Cr parameter in autodock?

When I run autogrid4 it says: autogrid4: ERROR: Unknown receptor type: "Cr" -- Add parameters for it to the parameter library first! Look forward to your reply.Thank you so much!

29 July 2024 488 0 View

Standard curve of H2O2?

Hi, I need to prepare a standard curve of H2O2 to evaluate the primary products of oxidation. H2O2 I have is 35%. How do I prepare a stock of H2O2 10 microlitere. If s.o has experience, I would be...

26 July 2024 3,460 2 View

How to do FEL analysis?

In molecular dynamics simulation, to get FEL analysis, I got an error. My Python version is 3.10.7. My input files are made with a lower version of Python. But the final command to generate the...

23 July 2024 5,646 2 View

What is the main factor involve in higher binding score performing molecular docking?

A molecule shows the -11.6 kcal/mol and second one -8.0 kcal/mol so why molecule (A) revealed higher binding score. Please explain major factor involve in it.

21 July 2024 954 5 View

How Can I Resolve a Persistent Unwanted NMR Peak at 1.25 ppm?

Hello everyone, I am facing a consistent issue in my NMR spectra with an unwanted peak appearing at 1.25 ppm. This peak seems to vary with the amount of sample: it becomes more pronounced with...

15 July 2024 9,065 4 View

Intracerebroventricular (ICV) AAV inj.?

I'd like to know if anyone has got experience in intracerebroventricular (ICV) AAV inj. I am looking for a concomitant spread of the AAV including but not limited to the motor cortex and the...

12 July 2024 781 0 View

Why PDMS is not hardening ?

I use PDMS to build a microfluidic system, but it is not hardening at all, although I use TEOS as a cross-linker and also ATPES in a ratio of 1:10, and it's been 3 days at 80 degrees of 3 ml cast...

01 July 2024 604 3 View

Chemical composition of curing agent for PDMS (Sylgard 184 Kit) and solid percentage?

1- Please provide information about the chemical composition of curing agent for PDMS(Sylgard 184 Kit)? 2- what dry solid percentage is obtained for a ratio of 10 to 1(PDMS to hardener)?

30 June 2024 6,814 2 View

How to reduce the permeability of pdms?

I want to trap fluid (water..) in the PDMS channel for a long time. After a short period, the channels become empty of fluid. Is there a way to reduce the permeability of PDMS?

17 June 2024 2,703 4 View

How to color PDMS?

Hi, I am trying to color a very thin (3um), spincoated layer of PDMS with a dye (I want to make the thin layer visible to the naked eye). Does anyone have experience with dyes/ colors and...

11 June 2024 7,330 2 View

What is name of this chemical reaction process?

My research object is changing terminal functional group of PDMS from -OH to -PO(OH)2. I know just one experiment recipe using furan, ethylamine, POCl3, D.I water. But it not work well. So i want...

09 June 2024 5,290 0 View

Why is my thin film PDMS TFM device warping only when with cells?

I've been fabricating traction force microscopy devices in glass bottom dishes, using a method that first spins a 100 micron PDMS layer, then a ~1 micron PDMS + fluorescent beads mixture layer....

09 June 2024 652 2 View

Is bonding PDMS to PI (Kapton) using a plasma treatment possible?

I’m looking into bonding a PDMS microfluidic circuit to a PI sheet using a plasma activation method. The PDMS will be on the order of ~700 um thickness, while the PI will be 12.5-50 um. I have...

24 May 2024 7,050 1 View

Is there a way to use Trichloro(1H,1H,2H,2H-perfluorooctyl)silane without using vacuum chamber?

I've been wanting to use 3D printed mold (resin) for curing PDMS for micro-contact printing. I figured that PDMS wouldn't come off that easily so silanization would be required however, I do not...

22 May 2024 4,809 1 View

Is there any flexible polymers similar to PDMS, but has hydrophilic property?

looking for a polymer which, 1) will be used for microchannel (cross-section: rectangle with 1.4-1.6 mm width, linear configuration) fabrication 2) easy to fabricate similar to PDMS 3) Permanently...

08 May 2024 6,472 1 View

Plasma bonding of PDMS to a thin glass (500 um or less). is it possible?

With oxygen plasma cleaner, i usually bond PDMS to 1 mm glass without any problem. Changing to 525um thickness glass, so far, I got one time success from plenty of failed attempts. Even in that...

25 April 2024 3,622 0 View