I would like to apply polyaniline coating in acidic medium, which is the best acid for coating by Potentiostat?
oxalic acid on oxidation will give carbon dioxide, avoid
use sulphuric acid
niline and pyrrole copolymers were synthesized for
different monomer ratios from a mixed
electrolyte containing 0.1M oxalic acid and 0.1M do
decyl benzene sulphonic acid (DBSA) using a 4-
step electrochemical method. Results were compared
to those obtained for polymers prepared from an
electrolyte of oxalic acid only. It was found that
the presence of DBSA increases the polymerization
rates for polymer deposited from the mixed monomer
electrolytes, but not for the homopolymers. For
copolymers deposited from monomer mixtures of high
aniline content, deposition rates were generally
low, due to the low conductivity of these samples.
FTIR and cyclic voltammetry results confirm the
presence of both monomers in the polymers deposited
from the mixed electrolyte, and FTIR indicates
that copolymers, rather than mixtures, are formed.
Results from AC impedance spectroscopy show that
the presence of DBSA results in an increased double
layer capacitance for the homopolymers and
increased low frequency capacitance for those sampl
es with low pyrrole content.
http://www.electrochemsci.org/papers/vol3/3091065.pdf
I am working on doping of carbon nanotube and I would like to know what is the best dopant and the easiest method for this?
01 February 2017 1,596 9 View
When we add any material to electrolyte of coating, how can we consider the additive if it is a dopant or only an additive according to the EDS analysis?
31 December 2016 3,168 13 View
If we would like to add some anions to polymer coating. What are the best as dopant using electrochemical method for coating?
08 September 2016 4,644 2 View
We would like to apply conductive polymer coating on metallic alloy. What is the best method for this?
06 July 2016 1,992 11 View
I fabricated nanowires and after complete dissolving of template, I need to obtain the dried nanowires. Can anyone help me to achieve this process?
04 May 2016 5,089 10 View
I have DSC for Al-Ti alloy and its composites with MgO and SiC and there are shifting in peaks to upper or lower regions, Please can any one help me to interpret them?
02 March 2016 9,264 4 View
I deposited nanowire by electrochemical method using AAO template and I would like to measure some properties of it. Can I achieve the measurement without dissolve the template?
02 March 2016 8,004 4 View
I have a paper about corrosion and I need to publish quickly.
01 February 2016 4,800 2 View
I fabricate nanowire and I would like to characterize it?
01 February 2016 7,453 4 View
Please can any one help me? I fabricated four aluminum matrix composite with SiC and MgO, and I need the best method to find the exact chemical composition after casting. What is the best method...
01 February 2016 1,081 14 View
How can I determine a good adhesion strength range for coatings on polymer surfaces, such as DLC on polymer substrates? Is there a specific threshold for adhesion strength (from T-peel tests)...
10 August 2024 942 3 View
I did PR spin coating on trench structure. I used AZ P4620 PR and the thickness or PR is around 11um. The substrate is Si. And my trench structure depth is 141um(negative way). Even though I...
08 August 2024 2,298 0 View
Hello What should be done to separate and identify organic acids in HPC when their RetTime is the same?Like oxalic acid with Propanoic Acid.or acids that have a very close RetTime.
07 August 2024 8,782 3 View
I have been getting a low plasma and no coating while doing rf sputtering of copper doped ZnS using a power of 140 watts and at pressure of 6.5x10-3 Mb.
07 August 2024 4,526 4 View
For example, I perform passivation process before electropolymerization of Py for adhesion to titanium surface. Is a similar or different procedure required for ITO? If necessary, I would be glad...
06 August 2024 3,176 0 View
Palmitic acid presence in aqueous fraction
05 August 2024 8,624 4 View
I used humic acid at 0.044 g/kg soil in my pot experiment. But finally, I have to recommend kg/ha. Each pot's soil weight was 11 kg. What is the solution?
02 August 2024 7,186 6 View
I am currently working on a project involving liposomes and need to determine the maximum volume of siRNA that can be added to a 2.5 mL liposome solution with a total lipid concentration of 10...
30 July 2024 6,420 1 View
Hello, I'm trying to measure the conductivity of semiconductor films but since I don't have a commercial four point probe set up I would like to build one on my own in my lab. I have generators,...
30 July 2024 906 2 View
I am trying to coat my micelles and PLGA based nanoparticles with cell membrane using an Avanti mini extruder according to literature . I use 200nm membrane but my particles end up to be 400nm And...
30 July 2024 3,294 3 View