I have DSC for Al-Ti alloy and its composites with MgO and SiC and there are shifting in peaks to upper or lower regions, Please can any one help me to interpret them?
Please, draw all signals on one plot. and provide some additional information - what is the gaseous enviroment, sample masses (if different in these three runs), confinemtn of the sample (open/pierced/closed pan)
In addition to Nikita's comments: please indicate if this is raw data or if you have already substracted the baseline. If no, please do so. This would explain the tendency of your curves going upwards/downwards (not including the exo/endo peaks).