I have plotted my VSM data in origin for a nano powder sample. I got a plot where the hysteresis behaviors' are not appropriately observed. When Magnetization is zero (y-axis is zero), both magnetic field values are negative........ similarly, when magnetic field is zero, both magnetizations are positive.
What does it indicates?? (Here, I have considered magnetic material only. - transition metal which exhibits magnetism).
What kind of magnetism is this?
Kindly help me out.
Could you provide a little more information about the type of material you are working with? At a first glance it looks like exchange bias, where you have a displacement of the hysteresis curve due to the exchange interaction between a ferromagnet and an antiferromagnet.
José Elias Abrão Neto sir, I have sent you a message regarding this.
Kindly check once
Thank you