Hello,
From existing literature aware that the two characteristic XRD peaks of g-CN are at 2θ 13 and 27 degrees approximately.
What I would like to know is the range of variation of these peaks, in particular the peak due to the in-plane arrangement of the triazane rings.
During my synthesis of g-CN, I had a peak at 14.6 degrees and 27.7 degrees.
I am concerned that the peak at 14.6 may be incorrect.
Can this peak due to the in-plane triazine arrangement shift or just get more intense? Depending on the order.
I would appreciate some guidance on this matter.
Thank you.
Hi Joshua Nigel Fernandes
Please do the XRD using the same as the reported literature (what you have stated as a referencing article) i.e., match the scanning time, range, etc., and then try to correlate the data.
Regards