Dear researcher
kindly suggest standard technique for electropolishing of sintered Titanium aluminide specimen for characterization
some researchers indicate in their article that
Struers A3 electrolyte
what is this A3 electrolyte?
during electropolishing, which materials should be selected as cathode
also it is mentioned that temperature during polishing need to be maintained at -40 deg C
how this low temperature need to be achieved, any suggestions.
regards
Dear Dr. Dhana Sekaran,
I think you can find useful information by consulting the following paper, point of reference regarding your question:
The characterisation of a powder metallurgically manufactured TNM™ titanium aluminide alloy using complimentary quantitative methods
Schloffer, M.; Schmoelzer, T.; Mayer, S.; Schwaighofer, E.; Hawranek, G.; Schimansky, F.-P.; Pyczak, F.; Clemens, H., Pract. Metall. 2011, 48, 594–604.
Best regards, Pierluigi Traverso
Dear sir,
You can try the electrolytes attached in the below file.
Thanks researchers for sharing the content
dear Dr. Pierluigi Traverso
the article that you quoted in the answer is restricted to download
will it be possible for you to send a mail to [email protected]
The characterisation of a powder metallurgically manufactured TNM™ titanium aluminide alloy using complimentary quantitative methods
Schloffer, M.; Schmoelzer, T.; Mayer, S.; Schwaighofer, E.; Hawranek, G.; Schimansky, F.-P.; Pyczak, F.; Clemens, H., Pract. Metall. 2011, 48, 594–604.
with regards
Dear Dr. Dhana Sekaran,
you can directly request to the authors, via ReserchGate (https://www.researchgate.net/publication/269525225_The_Characterisation_of_a_Powder_Metallurgically_Manufactured_TNM_Titanium_Aluminide_Alloy_Using_Complimentary_Quantitative_Methods) the cited article, indicating that you will use it for research purposes. There should be no problems, otherwise let me know.
Best regards, Pierluigi Traverso