in order to create GelMA and Carboxymethyl Chitosan Hydrogel Scaffolds? Do I need to use EDC/NHS for crosslinking ? OR Lithium acylphosphinate photo-initiator (LAP) is enough as the crosslinking and then exposure to light at ultra-violet (UV) (365 nm) wavelengths would be enough ?
Devis Montroni
You will surely have the Carb. met. chit entangled in the GelMa network and probably a fraction will be covalently binded, but I would not rely in that if you want a deep covalent interaction between the polymers. On the other hand, I feel that would be enough to have a solid quite interacting composite.