Depends on your substrate and the thin film you are depositing. There is no general rule that applies to all materials. And if you are creating interfacial layer.

For instance, you van deposit gold on silicon, but it changes with temperature. My work showed formation of gold silicide at lower temperature, total gold infusion in silicon at higher temperatures.