Hi,

You have to use solid state NMR. For this, you have to grind your glass samples and sieve it through 125 micron mesh. You can use that sieved powder with particle size less than 125 micron to fill the rotor. Ideally 300-400 mg sample is required. Hope, this will help to your question.