It depends on the coating process. For example, in the case of plasma sprayed coating, residual stresses are related to the coating thickness. But there is also species scattering through the interface, what create intermetallic species. This diffusion layer is presented in Barradas et al J. Mat. science 2004 p.2707-2716.