I would like to see an electrospun mesh under SEM after a coat with gelatin. My idea is to immerse de electrospun mesh in gelatin to perform the coating and then leave the sample in vacuum overnight.

Finally, I will coat the sample with palladium to make it conductive.

Is this process correct or should I add a dehydration process with ethanol gradients, for example?

Thank you!