You can perform volume scattering and measure the angular distribution of scattered light intensity. From the distribution, you can obtain a mean and stdev of the particle sizes.
all methods will give you differing information - you always need to have a deeper knowledge of these methods and their limitations. At 1 mass percent it will be almost impossible to obtain information on the individual particles as these will interact strongly, at least sterically.