Hi Saideep! A very good question. If you make a disordered/amorphous material, there can be significant changes in the conduction band and the band gap. In the extreme disorder case there can be even localisation of the electronic states. On the other hand, if you make an ordered superlattice with a large unit cell, the band structure becomes very complicated and the gap can strongly depend on the details of your structure.