Does anyone know the method of changing the as-welded columnar austenite microstructure into equiaxed austenite microstructure?

More Shitong Wei's questions See All

How could I get the P-value from the mean, SEM, and n of different groups in the t-test?

How could I get the P-value from the mean, SEM, and n of different groups in the t-test without the original data? For detail, I would like to know the P-value between BMP-2: 50ng/ml group and the...

06 February 2021 6,539 4 View

Why are my western blot bands so distorted?

Hi guys I'm out of ideas here please help! I've never had consistent problem like this doing westerns before and I can't figure it out. The condition used: - First 4 lanes have 50ug protein in...

04 February 2021 2,297 3 View

What are the possible drawbacks of using miRNA sponge to enhance the specificity of gene expression?

I am searching for miRNA repeats put between WPRE and 3'LTR of my lentivirus, in order to enhance the specificity of transgene expression in human neuron cells. But if clinically translation of...

26 December 2020 9,921 2 View

Can Apparent Activation Energy determine Conversion Rate in a catalysis reaction?

Recently, I got a concept that is contrary to my understanding from two papers. It can be described as follows, in brief: There are two catalysts for the same reaction, on the catalyst with higher...

09 December 2020 2,406 28 View

What is the standard preparation procedures of Powder X-Ray Diffraction (PXRD) sample?

Recently I started to use XRD to study the structure of some molecular sieves. My powder sample was prepared by grinding in a mortar, drying in an oven, and loading on the sample holder. However,...

03 December 2020 7,504 8 View

Could anyone professional help me to solve this problem?

I have installed the software BRUKER Flexanalysis 3.4 on my computer successfully. But when I tried to import the MS data produced by BRUKER MALDI-TOF-MS, I met with an error described in the...

10 November 2020 8,205 1 View

How to prove the hypermethylation of a certain gene inhibits the gene expression?

Hi, As described, recently we found a gene was silenced in various tumor, and its promoter was alwasy hypermethlated. When using certain treatment to induce the gene expression, we found its...

04 November 2020 7,054 3 View

Could anyone recommend a kit to isolate exosome from cell culture supernatant?

Hello, I'm working with immortalized HUVECs low and I'm trying to study their exosomal RNA contents. Could anyone recommend an effective kit to isolate exosomes from cell culture supernatant?...

31 October 2020 4,252 5 View

Is there a technique to implant a cannula for repeated CSF sampling?

We need to collect CSF samples repeatedly from the 4th or lateral ventricle of rats. Does anyone know of a protocol for implanting a cannula to be able to do this? Or even a protocol for this...

26 October 2020 5,804 3 View

Any ideas on how to prevent the mouse cornea cryosections from dehydration?

I am analyzing the tissue damage to the mouse cornea tissue after incubated a kind of medium. The protocol is 1) mouse cornea was incubated in the medium for one day 2) embedding the cornea with...

21 October 2020 7,568 5 View

What is the production process of CaFe ferroalloys?

I looking for ferro calcium production process

03 March 2021 1,755 4 View

12% ledeburitic cold work tool steel, etched for revealing retained austenite, any help for clarifying?

Hello everyone. Given microstructure image belongs to a 12% ledeburitic cold work tool steel (annealed and tempered). The sample was etched with picral (100 mL ethanol and 4 g picric acid). I...

02 March 2021 4,119 3 View

Why Austenite grains in steel show much more twinning than ferrite grains?

It is oftentimes said to be a distinctive metallographic trait that differentiates a fully austenitic and a fully felly ferritic steel without etching that might distinguish between two. Why...

02 March 2021 728 2 View

How Can I bring as much common elements in steel as possible to calculate stable phase(s) in OpenCalphad?

As I was tweaking step-by-step OpenCalphad6 Macros step1.ocm involving phase and thermal property calculation of a High-speed steel, I could not incorporate more than 6 elements in the steel...

01 March 2021 8,840 1 View

I need to accelerate corrosion in steel parts that are used in a salt-water environment. Is there a technique for doing so?

I have a structure that employs d-ring swiveling tie-downs that corrode during use and become "frozen". I have sample swivel assemblies that I wish to corrode to see if I can free them using one...

01 March 2021 3,739 3 View

Why is my platinum counter electrode getting dirty during electrodeposition?

I am conducting anodic electrodeposition of MnO2 onto a stainless steel substrate, using a platinum strip as a counter electrode. This is done galvanostatically, with the current held between 5...

27 February 2021 1,829 3 View

What kind of steel moulds are used for hot pressing metal powders?

My main concern is that the metal powders should not weld to the mold surface and I should easily be able to eject out the pressed samples. I am looking for alternative for graphite moulds. The...

22 February 2021 2,965 4 View

What are effects of steel jacketing on flexural strength?

Dear all, If steel jacketing is used to retrofit a reinforced-concrete (RC) column, can we use it to improve flexural strength? I understand that we leave gaps between the ends of the jacket and...

22 February 2021 1,906 5 View

How to model steel jackets using SeismoStruct?

Hi all, Does SeismoStruct support modeling rectangular RC columns retrofitted with steel jackets (e.g. rectangular, elliptical) ? Any suggestions for other software (apart from...

20 February 2021 4,521 1 View

Thermal and mechanical properties of concrete and steel after cooling?

How do the thermal conductivity, specific heat capacity, plastic strain, critical compressive displacement, and thermal expansion of both hot-rolled steel and concrete change after cooling based...

15 February 2021 1,385 5 View

Shitong Wei

This figure indicates the as-welded columnar austenite microstructure.

Belma Fakić

Dear,

Did you try heat treatment, put material at temp. high then austenitisation temp.?

Weld metal is cast microstructure.

Harald Rojacz

Heat treatment at certain temperatures (Normalising ~ 1000°C) for several hours should get rid of the as welded microstructure.

Dear Harald Rojacz. The weld metal is the full austensitic microstructure, how can we conduct the normalising treatment?