As you may know, the term steel encompasses an extremely wide range of alloys with very different properties depending on their microstructure. Some of them are very brittle (e.g. as-quenched high-carbon martensitic), others very ductile (e.g. interstitial free). Thus you can not compare "steel" to ductile iron but rather a given grade after a given treatment.