Dear All

Please, Can the incomplete binding between P25 (TiO2) and graphene oxide decrease the photocatalytic activity?

I prepared P25/GO using colloidal blending method and tried GO from different companies and prepared it by myself, but it still P25 has a higher activity than P25/GO.

I used this method of preparation P25/GO 1%:

an aqueous dispersion of graphene oxide (0.01) was dissolved in 30 mL of deionized water.0.99 g TiO2 powder (P25, Degussa) was dispersed in 50 ml deionized water and subsequently added to the graphene oxide solution. The mixture was sonicated for 1.5 h and further stirred for 12 h at room temperature to obtain a homogeneous solution. The product was filtered and

dried in a vacuum at 50 ◦C for 4 h.

I do not know what is the problem. Does P25 not have enough hydroxyl groups or what?