Hello!
I'm now working on the preparation of cellulose nanocrystline. I used a dialysis tube in my treatment. Is it okay if I use it again? Would you share your experience ?
Thank you
Generally, I would not reuse dialysis tubing because I would be concerned about the pores becoming clogged or microbial growth occurring.
If you are going to use it immediately you can do it.
But if you plan to store for several days or weeks it is not recommended.
Saludos.
Thanks sir for your answer
I do not advise You, to reuse dialysis set!
thank you for your answer
It is not advisable to reuse dialysis tubes due to contamination issues and changes in the dialysis properties.
VUMAT subroutine which describes cyclic constitutive model of steel bars which tell us the ultimate strain bars using FORTRAN language for ABAQUS user defined material.
04 November 2023 9,582 2 View
OriginPro (https://www.originlab.com) is one of my favorite software, especially for graphing. It can also do many statistical analyses. However, I can't do one-way ANOVA with RCBD design (i.e....
18 May 2023 6,385 2 View
The SEM results from my experiment revealed that the noncrystalline cellulose had a spherical form (CNC). The majority of paper written on CNC is rod shaped. Additionally, some papers demonstrated...
07 August 2022 8,386 1 View
I am working on Cellulose nanocrystaline, I got CNC suspension. but I want to know hoe the stabilities of CNC measured. Thank you very much for your help
25 May 2022 4,550 0 View
Currently we are planning to start an experment of feeding trial in chicken. We are testing different inclusion rate of diet X on the growrh perfirmance ,feed efficency ... My question is in meat...
23 March 2022 4,901 6 View
I need explanation. I am working in nanocellulose preparation in one species which has no any research work. But there are so many research work in another species of same genus. I need your...
22 December 2021 5,385 0 View
I am preparing crystalline nanocellulose in my laboratory. But I have a problem. How do I know if crystalline nanocellulose is is formed or not? I have a product in my hand but I want to know...
05 November 2021 9,470 5 View
I work in an organic chemistry laboratory and just encountered an issue with holocellulose preparation. I'm unable to obtain NaClO2. Do you believe that NaClO could be used instead of NaClO2? help...
22 July 2021 2,121 0 View
In an adsorption experiment, I will utilize the Langmuir isotherm model and the Freundlich isotherm model in my research. In my study article, I'd want to make a few explanation about the...
02 June 2021 9,530 4 View
Agriculture, which constituted 46 percent of GDP and more than 80 percent of exports, is by far the most important economic activity in the Ethiopian economy. An estimated 85 percent of the...
28 December 2020 3,698 3 View
I want to remove Urea from my protein (6kDa) sample. I did use : 1. Step down the Urea gradient (dialysis) in order to remove urea and refold my protein, but my protein still contains urea in the...
06 August 2024 1,350 4 View
kindly reply me. Thanking you in advance.
05 August 2024 7,727 4 View
Is it the "elution buffer" or the "dialysis buffer"? Note: I'll be using NanoDrop OneC
01 August 2024 967 3 View
I am conducting my research regarding blood coagulation in patients with CKD. I observed a reduction in post hemodialysis aPTT and PT values compared to pre hemodialysis values. But most of...
30 July 2024 3,467 0 View
Hi, researchers, Is it possible to use a safer acid instead of monochloroacetic acid to convert bacterial cellulose to carboxymethyl cellulose?
29 July 2024 4,570 0 View
Hello everyone reading this topic! It is well known that microcrystalline cellulose 102 is recommended for use in direct compression technology, however, like other grades, it has poor flowability...
08 July 2024 2,807 0 View
I use X-ray diffraction (XRD) techniques to quantify the degree of crystallinity in my samples, referring to the following formula (CrI=Acrystal-Aamph/Atotal ). using deconvolution area methods (...
06 July 2024 6,234 9 View
Hello, I am looking for (estimated) degradation rates of cellulose in a classic anaerobic digestion setup (meso or thermophilic, WWTP sludge, 30+ days of operation) to have an idea of the % of...
01 July 2024 5,867 5 View
I purified my recombinant GST-tagged protein in Tris buffer at pH 7.6 (the protein’s PI is 7.11) using a 50 mM reduced glutathione concentration in the elution buffer. However, after dialysis to...
21 May 2024 9,951 2 View
I am studying the surface topography of bacteria-degraded cellulose and lignin using the non-contact mode of Atomic Force Microscopy (AFM), which requires a solvent to make a dispersion of the...
21 May 2024 6,358 3 View