I synthesis ZnSe thin film using electrochemical deposition. Can anyone tell me why why I can not get ZnSe peaks? My electrolyte is ZnSO4+Seo4+H2O, PH=2-3 and bath temperature is 60-70C. The deopsition potential was -0.6V, -0.7V, -0.5V.
Hello. If your thin film is too thin XRD will not see it. The penetration of X-ray is approximately 1microm so most all your information comes from the substrate which in your case I understand it to be ITO. To see something with regular XRD you need to make your film thicker. Other problems may involve close proximity with bragg reflection peaks of your film with respect to peaks from substrate. Wish this helps you some. Cheers.
Another possibility is that your synthesized material is amorphous so in the XRD pattern no peaks are evident.