Presumably your vertical axis is force and horizontal axis is displacement and your forces are low enough to protect the sample from plastic deformation or failure.
If all cycles are performed to the same force, then viscoelastic relaxation or creep will cause migration of the minimum and maximum displacement. This effect is more pronounced in the first few cycles and diminishes with higher cycle numbers. This happens because biological tissues are not perfectly elastic.