Which method of coating is the best suggested for coating Reduced Graphene Oxide (RGO) on a Titanium material?

More Nithesh Naik's questions See All

Which method of coating is the best suggested for coating on a Titanium material?

I want to coat Titanium with RGP Graphene Titanium Nitride Hexagonal Boron Nitride for implant orthopedic applications. Please suggest best methods for the above

04 May 2019 3,443 3 View

Adhesion strength of coating?

How can I determine a good adhesion strength range for coatings on polymer surfaces, such as DLC on polymer substrates? Is there a specific threshold for adhesion strength (from T-peel tests)...

10 August 2024 942 3 View

How do I conformally do PR spin coating on trench structure?

I did PR spin coating on trench structure. I used AZ P4620 PR and the thickness or PR is around 11um. The substrate is Si. And my trench structure depth is 141um(negative way). Even though I...

08 August 2024 2,298 0 View

Why do i have a weak plasma and no coating during rf sputtering?

I have been getting a low plasma and no coating while doing rf sputtering of copper doped ZnS using a power of 140 watts and at pressure of 6.5x10-3 Mb.

07 August 2024 4,526 4 View

What is the best conditions for formation Magnetite ore deposits?

I want to know more about Magnetite deposits.

06 August 2024 1,066 0 View

Hello, regarding Mxene 2D titanium carbide?

I fabricated Ti3C2Tx using concentrated HF 40%, I plot an XRD as attached image below.. please let to know if I obtained it or not.

02 August 2024 6,789 4 View

Short Synthesis of Graphene Oxide from Natural Graphite Flakes?

I am in search of a modified Hummer's method, which can be used to synthesis graphene oxide within 6-8 hours. As I am a student it is not allowed for us to work after 5 in the laboratory. So I am...

01 August 2024 8,368 2 View

How can I separate graphene from amorphous carbon of similar particle sizes?

The starting material is a finely ground powder. Some particles contain more graphene than others.

30 July 2024 3,978 2 View

Ti6Al4V - Phase differentiation between alpha and alpha prime martensite?

Dear Researchers, Is it feasible to distinguish between alpha and alpha prime martensite in the Ti6Al4V alloy under rapid solidification in the as-cast state using XRD, in addition to...

30 July 2024 3,849 0 View

What is the reason I get 400nm nanoparticles using an extruder with 200 nm membrane for cell membrane coating?

I am trying to coat my micelles and PLGA based nanoparticles with cell membrane using an Avanti mini extruder according to literature . I use 200nm membrane but my particles end up to be 400nm And...

30 July 2024 3,294 3 View

What is the solubility of Iron (+3) in Bismuth Oxide?

Dear all: I am modifying Bismuth Tungstate with Hematite (Fe2O3), so I would like to know about how much Iron(+3) can form a solid solution in a Bismuth Oxide matrix. Best wishes Marco

29 July 2024 2,163 1 View

Haider Abdulkareem Al-Mashhdani

I suggest EPD

Zoraida P Aguilar

The answer to your question depends on why you want to coat the RGO on Ti. First, analyze why you want to coat it. Next, analyze what the surface charge is before coating. Then. find out what materials are best for these conditions.

Ahmed mohammed Jasim

What is the clue of coating TiO2? By itself a stable