What is the maximum fiber diameter which can be obtained using electrospinning?

error in running a model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

error in modelling model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

MGL tools

20 June 2021 0 0 View

How climate change will influences human and animal behavioral change?

The role of climate change influencing the human behavior as well as economics interest

01 June 2021 0 0 View

what is the simplest definition of ion exchange capacity

What this unit identifies for the ion exchange capacity ca. 0.92 meq. g-1. I am a newcomer in the membrane area. I just started. I highly appreciate your help

08 May 2021 0 0 View

what is the simplest definition of ion exchange capacity

What this unit identifies for the ion exchange capacity ca. 0.92 meq. g-1. I am a newcomer in the membrane area. I just started. I highly appreciate your help

08 May 2021 0 0 View

flexibility of polymers chain

effect of double bond on the flexibility of polymers

07 April 2021 0 0 View

i have some problem with chtMultiRegionSimpleFoam

--> FOAM FATAL ERROR: Maximum number of iterations exceeded From function Foam::scalar Foam::species::thermo::T(Foam::scalar, Foam::scalar, Foam::scalar, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar) const) const [with Thermo = Foam::hConstThermo >; Type = Foam::sensibleEnthalpy; Foam::scalar = double; Foam::species::thermo = Foam::species::thermo >, Foam::sensibleEnthalpy>] in file /home/ubuntu/OpenFOAM/OpenFOAM-4.1/src/thermophysicalModels/specie/lnInclude/thermoI.H at line 66. FOAM aborting #0 Foam::error::printStack(Foam::Ostream&) at ??:? #1 Foam::error::abort() at ??:? #2 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::calculate() at ??:? #3 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::correct() at ??:? #4 ? at ??:? #5 __libc_start_main in "/lib/x86_64-linux-gnu/libc.so.6" #6 ? at ??:?

24 March 2021 0 0 View

Formulation of polymer color flakes

I am writing to request some information for making polymer color flakes. I would appreciate the help.

17 March 2021 0 0 View

Can we classify HV and LV lines based on line length?

I have dataset which shows the length of power lines. I need to classify the lines based on the line length. Is there a rule to classify the High voltage (HV) and low voltage (LV) lines based on...

03 March 2021 4,116 4 View

Salah A Elsheikhi

Hi, If you are looking for the nano-fiber diameter and its length; this paper may help you:

https://www.ncbi.nlm.nih.gov/pmc/articles/PMC3065832/

Danila Petlin

Dear Prosper, any synthetic biodegradable polymer - solvent system, maximum voltage I can get on the system we use is 30 kV. But what I really wanted to find out, is what is the theoretical maximum diameter possible to be achieved.

Dear Salah, I have used different biodegradable polymers for the fabrication of nanofibers, included PCL to which the paper you provided is devoted. So, it is easily possible to make fibers more than 2 mkm. Thank you for your time anyway

Ipek Yalcin Enis

Hello Petlin,

You should specify the polymer types and solvent systems. It is not possible to get sameresults for all biodegradable polymer solutions and, voltage by itself is not enough to determine all production parameters that influence fiber diameters.

For instance for PCL/Chloroform solution, fibers diameters of 5 um can be produced homogenously.

Ali A Salifu

Dear Petlin

In addition to the polymer type and solvent, the maximum fibre diameter will depend on the solution concentration you are using and the type of collector.