Hi researchers!
I would like to get your suggestions on powder XRD data.
Recently I found the peak (100 % Relative intensity) at 2theta= 36 degree in diamond film in addition to peak at 2theta= 44 degree.
Reported peak of (111) in diamond is often found at 2theta= 44 degree.
So now my questions is that what could be the significance of this peak at 36 degree? This peak is probably not reported in any article. If yes then kindly share the information of that powder XRD pattern.
I am also attaching one well reported powder xrd pattern by other authors in this question.
Looking for your suggestions.
The peak at 2 theta = 33 degree is the peak for the plane (200).
Article N-diamond: An intermediate state between rhombohedral graphi...
Dear Dr.Valentin Bogatu,
Thank you for the information.
But in my case peak at 33 degree is the stongest peak compare to reported peak of diamond at 44 degree. I obtained two stong peak one at around 33 degree stongest and another at 44 well reported...
So why i recieved stongest peak at 33 instead of 44?