No problem with LiF. Thermal or E-beam evaporation. Ni, Ta, W, Mo crucibles and boats work. Slight preheating of material suggested to remove moisture.
TPBi is a fully different world - main problem is to find low enough temperature to avoid breaking of the molecule.