Pl give inputs for calculating current density in electrocoagulation?

Pratibha Gautam @Pratibha_Gautam4

08 August 2019 1 6K Report

It may be assumed that Current is 2.5 A and electrode plate have length : 10cm, width 6 cm and breadth 1 cm.

Need to calculate current density for electrocoagulation.

Marie Berthuel

Pratibha Gautam

The current density is : j [A.cm-2] = I [A] / S [cm2]

Since you know the surface of your plate, the calculus will be pretty straight forward.

Best regards,

Marie B.

Badges
Science topic

More Pratibha Gautam's questions See All

Not getting repeatability in Electrocoagulation.

I am not able to get similar results while repeating same experiments for treating leachate through electrocoagulation. Results are not even comparable. What can be the reason.

01 January 1970 8,342 11 View

Waters 2707 HPLC autosampler problem?

I am using a 2707 waters HPLC device. When I try to inject a sample, it says missing plate or rack. I changed the needle and calibrated its position but I still get the same problem. I even get...

02 March 2021 1,408 1 View

Should we change media after1st 6hrs after plating HUVEC bought from INVITROGEN?it's not recomended by invitrogen.Will DMSO present in stock matter?

We have HUVEC bought from Invitrogen. Cat no -C-003-5c. while first plating the cells we have bought the protocol suggests not to centrifuge the cell with media to remove the DMSO. Should we...

02 March 2021 3,713 2 View

How to normalise data on OPM package from R Studio ?

Good afternoon, I recently used OmniLog from BIOLOG for my experimentations : I tested the metabolism of different strains on 2 types of plates. I have 16 strains of 3 different groups...

02 March 2021 3,584 1 View

Sutter electrode holder leaking after applying positive pressure. How to fix?

I am using a Sutter electrode holder for my patch clamp experiments, but I'm having trouble keeping positive pressure inside my electrode due to a leak out of the back of the holder. I have added...

02 March 2021 5,829 1 View

What thickness need for ITO to use as conductive layer?

I want to do RF sputtering of ITO on glass substrate using magnetron sputtering. what thickness do i need to make it good conductive layer to use it for PSC. Moreover, whats about thickness of...

01 March 2021 395 3 View

Benefits of the 24 welled plate?

We have always used the 96 welled plate, the 48 welled plate but apparently there is much evidence on the 24 welled plate and above all its benefits.It states it is the same you would use on ELISA...

28 February 2021 1,149 1 View

Can bacterial suspension be pipetted directly onto petri dish and agar poured onto it?

Hi, recently I encountered a protocol for plating which was not the usual method I have been practicing (pour LB agar onto plate, allow it to solidify, pipette bacterial suspension onto plate,...

28 February 2021 7,292 3 View

Why is my platinum counter electrode getting dirty during electrodeposition?

I am conducting anodic electrodeposition of MnO2 onto a stainless steel substrate, using a platinum strip as a counter electrode. This is done galvanostatically, with the current held between 5...

27 February 2021 1,829 3 View

What is the best surface to culture cells isolated from a skin biopsy?

Hello, recently I am having some difficulties with maintaining the cell culture of primary cells isolated from a skin biopsy (normal and malignant). The coating of culture plates with Matrigel (a...

26 February 2021 6,151 2 View

How does charge on working electrode changes with rising potential?

During performing CV of a GCE or modified GCE, we rise the potential in the first half of the cycle and reduce it in reverse half. During the first half, what is the nature of charge on GCE or...

25 February 2021 7,994 3 View