I've been struggling on a specific subject for a while. Hence, I'd like to get some advice. I am working on Mo-0.5 Ti alloy production via powder metallurgy technic. I have some problems with strenght. It is not high enough and I'm thinking to bring on new step of the process. Forging for final product. There are limited information on internet about Mo Forging. My question is what are the forging parameters(temp. etc.) for Mo.
Any help would be appreciated.
Thank you
Maybe take a look at ASTM A182-F1 for C-1/2Mo which is very strong. That spec might be helpful to you.
Another thought is to add chromium. Of course that is more expensive, but Cr-1/2Mo (ASTM A387-12) is used for high temperature pressure vessels. It's got the benefit of some corrosion resistance also.
Yeah but I can not change the composition ! That’s what bothering me actually