You can try spin-coating method, or reference graphene nanosheets dispersion method

If you are looking for very thin layer (nm thick) then spin-coating should be okay. You can use any additive layer to increase the adhesion of the 2D TMDs to the substrate to increase your deposition yield. If you are looking for very thick layer (um thick) then you can try spray coating.

Here are some examples:

http://pubs.acs.org/doi/pdf/10.1021/acs.chemmater.7b01605

http://www.sciencedirect.com/science/article/pii/S0008622310000965

Thank you very much Yangping Wen and Chandan Biswas for really important suggestions. I have initiated my efforts to make it. Let's see how it goes!

Thanks a lot..