In DSC heating rate was 10°C/Min in the range of 70-150°C. The heat flow vs. temperature curve was almost flat. But after the run, when lid was broken it was observed that the sample was melted within this temperature range. The same observation of melting was observed at around 105°C in melting point apparatus. How this is happening in DSC?