I am working in deformation and processing of Fe-Si alloy. I found difficulties in determine Tnr temperature of Fe-Si alloys. Kindly, anyone can help me to find Tnr.
Eventually, if you do not have access to a thermo-mechanical simulator, you can estimate Tnr using mean flow stress data got from hot rolling tests carried out at a laboratory or industrial rolling mill. See, for example,
You can determine Tnr temperature through multi-hit deformation test. This test generally carried out using thermo-mechanical simulator. If you do not have that facilities you simply can be estimate the approx Tnr temperature using Boratto equation. Here I have attached few link for your convenience.
Eventually, if you do not have access to a thermo-mechanical simulator, you can estimate Tnr using mean flow stress data got from hot rolling tests carried out at a laboratory or industrial rolling mill. See, for example,
There is a paper looking at the influence of Si on Tnr that you might find useful.
L. JIANG, A. O. HUMPHREYS and J. J. JONAS " Effect of Silicon on the Interaction between Recrystallization and Precipitation in Niobium Microalloyed Steels" ISIJ International, Vol. 44 (2004), No. 2, pp. 381–387