Harkins Jura isotherm:
This isotherm is mainly intended to calculate the micro pore volumes.
The plot for Harkins Jura is called as t-plot.
In X-axis it is statistical thickness calculated from Harkins Jura correlation:
Statistical thickness, t = [ 13.99 / ( 0.034 - log(P/Po) ) ] ^ 0.5
In Y-axis it is the Quantity adsorbed (cm3/g at STP), this will be obtained from adsorption isotherm (typically nitrogen adsorption isotherm) data, the specific (P/Po) value statistical thickness calculated.
As for the FHH plot, please, see my article about doping silica/titania with CuO/NiO. I used it to estimate fractal dimension. The purpose of the FHH plot is to establish by means of Ds morphological type of the nanostructure, whether aggregates or agglomerates of aggregates were formed. Your welcome!
bonjour, svp, comment calculer le diamètre moyen des pores du CAG , à partir des résultats de BET. merci beaucoup
Bonjour, svp quelle sont les informations que nous pouvons tirer à partir de la courbe linéaire de t-plot qui donne la variation de volume adsorbé sur un matériau poreux?. Merci d'avance.
Chère Rachida Cheblaoui; Chaque modèle a sa propre hypothèse. Ainsi, quel que soit le modèle auquel correspondent les données expérimentales, on considère que la cinétique d'adsorption est réalisée conformément au postulat de ce modèle. Le modèle de Weber-morris est basé sur la diffusion interparticulaire. Le modèle de pseudo-second ordre (PSO) est adapté à la chimisorption. Le modèle PSO nous donne également la valeur qe.