I use the phenomenological model for the crystal plasticity simulations, where the shear strain can be taken as output. However, I require the shear strain rate on individual slip planes to calculate the slip activity. Is there any post-processing method to evaluate individual shear strain rates on each slip system in DAMASK?
Sharan Roongta
Manoj Singh Bisht You can do this calculation as a post-processing step.
You have the information of the shear ("gamma_sl") for individual slip system in each material point, and each output increment.
You also have the information about the current time at every increment. So, the rates could be easily calculated?
Hope this helps,
Sharan