Dear Safya Elsharkawy

I think you are good! Yes, you can explain the electrodeposition using this curve. To get uniform deposition, stirring is good option to do. It will always provide the fresh ions to contact the electrode surface to deposit.

Best Regards,

Bapi

chronoamperiometry should always be done under stirring to keep the solution near the elctrode homogenous.

Bapi Bera thank you very much for your interest

Hello.

Yes it is better to use agitation. The best is use a RDE and do the experiment with different rotation speed. In this case, you could evaluate a diffusion coefficient.

Best Regards

Thomas