We deposit A-Si with 560C on oxide film. And we got tensile stress. Because we dop P on A-Si.
We can not use much lower stress as dep A-Si, because we must use annealing to active Poly, at the same time release stress. But at this moment we can not get the accurate formula about anneal temperature/time, that's why I ask here.