Dear Ali

hope so that you looking for TTT diagrams similar material

for example: steel x210Cr12

this steel has approxim. the same content of C but Cr is less

but if we know that Cr extend alfa range, and if you do not have another alloyed element in your cast iron you can try with information for this material

GOOD luck

Dear Fabkic

Thank you very much. Is it possible to have TTT diagram for this type of cast iron?

Best regards

Ali Ataiwi

I think TTT diagram will help, but with today technology if you put 2% copper you will tremendously increase your wear resistance. I did so many experiments on these types of alloy and optimize between 1 and 4% copper to find out that

austempering and martempering will increase their resistant with 2% copper.