About forging of Mo Alloys ?

Hello dear Academicians, I am working on the forging of Mo alloys, but I wanted to consult you on an issue I could not solve. Mo is easily oxidized during forging and MoO3 is formed. Is it...

09 February 2021 1,989 3 View

Molydenum Alloys Forging Process ?

Hello dear Academicians, I've been struggling on a specific subject for a while. Hence, I'd like to get some advice. I am working on Mo-0.5 Ti alloy production via powder metallurgy technic. I...

20 December 2020 3,805 2 View

How to distribute Titanium in Molybdenum host material via PM?

Hello dear Researchers, I've been working on to produce Mo-Ti alloys via powder metallurgy method. Yet, I've come across a problem: I can not properly distribute Titanium in Molybdenum host. I'm...

10 August 2020 4,502 3 View

How to distribute Titanium in Molybdenum host material via PM?

Hello dear Researchers, I've been working on to produce Mo-Ti alloys via powder metallurgy method. Yet, I've come across a problem: I can not properly distribute Titanium in Molybdenum host. I'm...

10 August 2020 5,909 4 View

How to peel off PDMS film from a glass petri dish without damaging it ??

I have prepared 15wt.% PDMS and poured it on a glass petri dish, then let it dry for 72 hr at room temp. after I tried to peel it and it doesn't work, so I am crosslinked in an oven for 3 hr , but...

26 July 2020 9,892 2 View

What is the best solvent for PVDF ?? Dimethyl sulphoxide or Dimethylacetamide??

For membrane preparation PVDF will be used , and I was wondering which solvent is the best for dissolving it, non-Toxic solvent , useful in dissolving other polymers such as PES, PDMS, Peba

05 July 2020 1,655 5 View

Are there any good data-sets or research papers/code for Deep Learning Model for medical 3D Construction from 2D CT Images?

I want to create a Deep Learning Model for 3D Construction of Breast Cancer in CT Images. However, I cannot find an appropriate data-set or research paper. The data-set should be multiple CT scans...

04 March 2020 3,614 3 View

I need a conference paper published in a conference book in 1998. Can anybody help me in getting this conference paper?

High Fidelity Mathematical Modeling of Reaction Wheel Performance (AAS 98-063) Bialke, B. /Guidance and Control 1998. (Advances in the Astronautical Sciences )

26 January 2020 813 2 View

Which type and size of beads are the most suitable for homogenizing the large intestine of rats?

There are too many information about this topic presented below: 2.4 mm Metal (Steel) Beads are recommended for hard tissues, skin, muscle, bone, hair 2.8 mm Ceramic Beads are recommended for...

15 November 2019 3,799 3 View

Can you help me with the conversion of the given bond diagram to block diagram ?

Does anyone have any clue or idea about drawing block diagram of this bond graph ? This problem is very important for me so any little help is appreciated. Thanks.

10 June 2019 4,427 1 View

error in running a model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

error in modelling model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

MGL tools

20 June 2021 0 0 View

How climate change will influences human and animal behavioral change?

The role of climate change influencing the human behavior as well as economics interest

01 June 2021 0 0 View

flexibility of polymers chain

effect of double bond on the flexibility of polymers

07 April 2021 0 0 View

i have some problem with chtMultiRegionSimpleFoam

--> FOAM FATAL ERROR: Maximum number of iterations exceeded From function Foam::scalar Foam::species::thermo::T(Foam::scalar, Foam::scalar, Foam::scalar, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar) const) const [with Thermo = Foam::hConstThermo >; Type = Foam::sensibleEnthalpy; Foam::scalar = double; Foam::species::thermo = Foam::species::thermo >, Foam::sensibleEnthalpy>] in file /home/ubuntu/OpenFOAM/OpenFOAM-4.1/src/thermophysicalModels/specie/lnInclude/thermoI.H at line 66. FOAM aborting #0 Foam::error::printStack(Foam::Ostream&) at ??:? #1 Foam::error::abort() at ??:? #2 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::calculate() at ??:? #3 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::correct() at ??:? #4 ? at ??:? #5 __libc_start_main in "/lib/x86_64-linux-gnu/libc.so.6" #6 ? at ??:?

24 March 2021 0 0 View

Formulation of polymer color flakes

I am writing to request some information for making polymer color flakes. I would appreciate the help.

17 March 2021 0 0 View

What's the best way to measure growth rates in House sparrow chicks from day 2 to day 10?

What's the best way to measure growth rates in House sparrow chicks from day 2 to day 10? Since, the growth curve from day 2 to 10 won't be like the "Logistic curve" it might not follow logistic...

03 March 2021 1,401 3 View

What is the production process of CaFe ferroalloys?

I looking for ferro calcium production process

03 March 2021 1,755 4 View

Resistor definition in Piezoelectric bimorph with ANSYS workbench

Hello, good day! I am trying to simulate similar bimorph piezoelectric harvester with below commands. However, the output power doesn't change with resistor value. Please help to find the reason. ET,10,CIRCU94,0 !SET UP RESISTOR R,1,100000 !RESISTANCE VALUE TYPE,10 !SET ELEMENT TYPE E,1,2 !CREATE RESISTOR BETWEEN NODES 1 AND 2 Thanks in advance Regards,

02 March 2021 0 0 View