I would like to dissolve preferentially potassium titanate and mixed oxides of calcium and titanium in a pseudobrookite (iron titanium oxide) matrix. Do you have experience in how one can do it? Thank you in advance for your answers!
I have little experience in dissolving & leaching of organic & organometallic mixtures & not those you mentioned. However, I found an article "I admit that it is lengthy" which may help. The good thing is that it is up to date & includes many references. My regards.
http://pubs.rsc.org/en/content/articlehtml/2015/gc/c4gc02360a
Thank you very much! I will definitely read through and I hope to get an idea of a leaching procedure. Best regards and one more time thank you for the quick answer.
put some of your grinded powder in a teflon-lined autoclave and add some chlorhydric acid (c.a. 5M), put in a 180 \celsius{} environment for 10 hour. it will be solved.