I prepared a graphene using Sonication assisted LPG. and this is a raman spectrum for a powder sample of this graphitic material, how can i estimate the number of layers using the 2D band Data?
Yes, smoothen your spectra first there is a lot of noise in the spectra. After elimination, you can easily find the peaks corresponding to the graphene from existing literature.
If I look at this, it looks like it has only 5-6 data points per peak. I would be fine with a coarse peak intensity ratio from this, but I wouldn't use this for shape analysis.
Here you see the degree of detail required for a shape analysis: