Actually, I have deposited some polymer films on Si/SiO2 wafers and I want to pyrolyze this films. I need very high temperature pyrolyzation for these films, up to 3000 C. I want some other high temperature sustainable substrate on which I can deposited the polymer thin films.
You can use Tungsten (W) or Graphite plates as substrate, I am sure it will fulfill your requirements. Its (W) melting point around 3422* C. You can use SiC also as substrate, Beside some oxide such as Al2O3 can resist at high temperatures.
I would suggest using Tungsten substrate, but it also depends on how are you going to heat them. I am curious to know why are you looking for such a high temperature (3000*C) to pyrolyze a polymer. I believe you will be using an induction furnace for the pyrolysis experiments, my friend earlier used graphite crucibles but we found there is carbon emission from the crucibles when treated with 3000*C. All the best
Thank you Satya for your suggestion. Actually I am doing some curiosity driven experiment with such high temperature. After completion I will definitely inform you.
Hey Kunal
Did you find a relevant solution to your problem?
I have a similar problem and really wish to know what you did to find a solution?
Can graphite plate and Tungsten if used for your purpose, be reused again or you have to discard them each time you use them?
Thanks.